Ti 6Al-4V

UNS #R56400

Ti 6Al-4V offers a combination of high strength, light weight, formability and corrosion resistance which have made it the most commonly used titanium alloy. It is an alpha+beta alloy that is heat treatable to achieve moderate increases in strength and is recommended for use at service temperatures up to approximately 660°F (350°C). Ti 6Al-4V may be considered in any application where a combination of high strength at low to moderate temperatures, light weight and excellent corrosion resistance are required.

Type Analysis

Carbon (Maximum) 0.1
Titanium (Nominal) Balance
Iron (Nominal) 0.4
Aluminum (Nominal) 5.50-6.75
Nitrogen (Maximum) 0.05
Hydrogen (Maximum) 0.015
Oxygen (Maximum) 0.02
Vanadium (Nominal) 3.50-4.50

Downloads

Request a Quote

Applicable Specifications

A5.16 (ERTi-5) (Weld Wire)
AMS 4905 (Plate
Annealed)
AMS 4930 (Bar
Wire
Forgings
Billet
Annealed)
AMS 4956 (Weld Filler Metal Wire)
AMS 4998 (Powder)
ASTM F620 (Forgings for Surgical Implants)
AMS 4907 (Sheet
Strip
Plate
Annealed)
AMS 4931 (Bar
Wire
Forgings
Billet)
AMS 4996 (Billet)
ASTM F136 (Wrought Alloy for Surgical Implants)
AWS A5.16-70 (Weld Filler Metal Wire and Rod)

Bar

Rounds

Shapes

Ultrabar Precision Bar

Ingot

Strip

Sheet

Wire

Dynalube Coil

Shapes

Smart Coil Titanium Coil

Weld Wire